J-600 & J-600B High-speed jet weaving slurry
- 产品详情
Chemical components:
Acrylic Copolymer
Chemical structure:
CH2-CH-CH2-CH-CH 2- CHC2CHn
COON H 4CO OR 1COON H 4CO OR2
Technical index:
Features and uses:
1. The slurry has low viscosity and excellent wettability and permeability to silk.
2. It has better adhesion to fibers, unique cohesion and abrasion resistance, which is conducive to high-density and high-speed weaving.
3. It has excellent smoothness, moisture resistance and excellent antistatic properties, and no falling size and re-sticking phenomenon during weaving.
4. It can be applied to various specifications of polyester and nylon fine denier, super fine denier and heterosexual bright yarn. Chemical structure.
Compliance with EU testing regulations:
1. Product specific requirements are based on ROHS Directive 2011/65EU: "Directives of the European Parliament and the Council of the European Union on Restricting the Use of Certain Hazardous Substances in Electrical and Electronic Equipment",
Test report number: TR20140151
2. The product complies with EU regulations (EC) NO1907/2006, referred to as REACH regulations, test report number: TR20140150
3. The product has passed the inspection of CRS organization and does not contain nonylphenol (NP), report number: RT-TSO-2013001677
Requirements:
1. When mixing the slurry, the water temperature is increased to 60℃, then the slurry is added and stirred for 20-30 minutes, and finally adjusted according to the required concentration.
2. The size of the slurry concentration affects the sizing rate. Generally, a high concentration also has a high sizing rate. The sizing rate required for different types of silk pairs is also different, so the sizing concentration must be reasonably controlled according to different varieties.
3. The sizing temperature directly affects the viscosity and sizing rate of the slurry. In order to obtain a uniform sizing rate, the temperature must be kept stable, generally controlled at 40-50°C. Too high temperature will easily cause the slurry to volatilize too fast.
The phenomenon of sizing liquid will affect the quality of sizing.
4. When sizing, the slick oil on the slurry in the slurry tank should be removed regularly, otherwise the sizing quality will be affected.
5. The water used for mixing and spraying water should meet the soft water requirements, otherwise it is easy to cause falling slurry and unclear desizing.
6. The slurry is anionic and should not be mixed with other cationic substances.
7. The slurry generally does not need to add other additives.
Reference sizing process:
Factors affecting weaving:
1. Slurry concentration: If the concentration is too high, the slurry permeability will be poor, and there will be back stickiness, falling slurry, unclear openings, difficult desizing or unclear desizing during weaving; the slurry concentration is too low to reach the sizing It is easy to produce hairiness and broken silk.
2. Drying: Failure to dry completely during the drying process can easily cause undesirable phenomena such as falling pulp and sticking. Excessive drying will cause static electricity, which will result in hairiness and broken filaments, which will affect weaving.
3. Workshop temperature and humidity: The relative humidity of the temperature and air in the workshop has a certain influence on the drawing, sizing, paralleling and weaving. Too high relative temperature will cause re-sticking and pulp shedding. If the relative temperature is too low, static electricity will be generated, which will cause fluffing. Unclear speech. Suitable temperature and humidity in the weaving workshop: Temperature: 20℃-25℃ Humidity: 65-75%RH
4. During the sizing process: After the slurry tank is heated, the water in the slurry will continuously evaporate by 1-2kg/hour (moisture). In addition, the water carried by the warp in the slurry is more than that of the slurry, so the viscosity of the slurry in the slurry tank will be reduced. As it increases, it will affect the quality of the sizing. In order to prevent the viscosity from increasing, new slurry should be added evenly for adjustment when changing the warp beam.
5. For silk with a large amount of oil adhesion: due to the high oil dosage of the original silk, it is easy to cause poor adhesion with the slurry, and the slurry film cannot be formed completely to weaken the water resistance, and the slurry is easy to fall off and re-stick, so it can be appropriately increased The temperature of the slurry tank and the appropriate increase of the pressure of the soaking roller.
Calculation formula:
Packing, storage and transportation:
1. The slurry is packed in 1000kg iron-plastic drum.
2. The slurry should be loaded and unloaded lightly, stored in a cool and ventilated place, and the storage period is six months.
3. The slurry is non-toxic, non-flammable, and can be stored as non-dangerous goods.